Matla a Motlakase a Ts'ebetso ea Graphite Electrodes
Tlhaloso ea Sehlahisoa
RP | HP | UHP |
Electrode: | Electrode: | Electrode: |
Boima ba Bongata≥ 1.56g/cm3 | Boima ba Bongata≥ 1.65g/cm3 | Boima ba Bongata≥ 1.68g/cm3 |
Ho hanyetsa ka ho Khethehileng≤ 8.5μm | Ho hanyetsa ka ho Khethehileng≤ 6.5μm | Boiketlo bo khethehileng≤ 5.8μm |
Matla a ho Kobela≥ 10.0MPa | Matla a ho Kobela≥ 12.0MPa | Matla a ho Kobela≥ 16.0MPa |
Elastic Modulus≤ 9.3GPa | Elastic Modulus≤ 10.0GPa | Elastic Modulus≤ 14.0GPa |
Katoloso ea Mocheso≤ 2.7x10 -6/°C | Katoloso ea Mocheso≤ 2.2x10 -6/°C | Katoloso ea Mocheso≤ 1.9x10 -6/°C |
Molora≤0.5% | Molora≤0.3% | Molora≤0.2% |
Nipple: | Nipple: | Nipple: |
Boima ba Bongata≥ 1.68g/cm3 | Boima ba Bongata≥ 1.74g/cm3 | Boima ba Bongata≥ 1.76g/cm3 |
Tšimoloho e Khethehileng≤ 7.0μm | Ho hanyetsa ka ho Khethehileng≤ 5.5μm | Ho hanyetsa ka ho Khethehileng≤ 4.5μm |
Matla a ho Kobela≥ 14.0MPa | Matla a ho Kobela≥ 16.0MPa | Matla a ho Kobela≥ 18.0MPa |
Elastic Modulus≤ 13.7GPa | Elastic Modulus≤ 14.0GPa | Elastic Modulus≤ 16.0GPa |
Katoloso ea Mocheso≤ 2.5 x10 -6/°C | Katoloso ea Mocheso≤ 2.0 x10 -6/°C | Katoloso ea Mocheso≤ 1.4 x10 -6/°C |
Molora≤0.5% | Molora≤0.3% | Molora≤0.2% |
Ntho | Boleng |
Sebaka sa Oriqin | China |
Mofuta | Thibelo ea elektrode |
Kopo | Indasteri ea Metallurgical |
Bolelele | 2000mm-2700mm |
Khanyetso (u2.m | 4.0-8.8 |
Boima bo hlakileng(g/cm | 1.55-1,82 |
Themal Expansio | 1.1-2.6,1.1-1.4 |
Matla a Flexural (N/m2 | 28Mpa |
Lebitso la Sehlahiswa | UHP Kereiti ea Graphite Electrode |
Lintho tse tala | Petroleum Coke |
Kolo | Ntsho |
Nnyo | 3TPI/4TPI/4TPIL |
Kopo | Smelting Stee |
MOQ | 20 Tor |
Deeistance/ | 4.8 ho isa ho 5.8 microns |
Boima bo hlakileng | 1.68-1,75 |
Matla a Flexural | 10-14 mpa |
Pacing | Linyeoe tsa Lehong |
Li-electrode tsa graphite li fana ka conductivity e phahameng ea motlakase, ho hanyetsa mocheso o phahameng, le matla a mochine. Melemo ena e etsa hore e be ea bohlokoa ka har'a libono tsa motlakase tsa arc bakeng sa tlhahiso e sebetsang ea tšepe le tšepe. Li-electrode tsa graphite li bonts'a melemo e mengata ea bohlokoa e etsang hore e be ea bohlokoa haholo lits'ebetsong tse fapaneng tsa indasteri. Ts'ebetso ea bona e ikhethang ea motlakase e nolofalletsa phetisetso e nepahetseng ea matla ka har'a libopi tsa arc tsa motlakase, tse bohlokoa bakeng sa ho qhibiliha le ho hloekisa litšepe nakong ea tlhahiso ea tšepe. Ho hanyetsa mocheso o phahameng ho lumella li-electrode tsa graphite ho mamella mocheso o feteletseng, ho netefatsa ts'ebetso e tsitsitseng le e ka tšeptjoang libakeng tse boima.
Kopo
Li-electrode tsa graphite li sebelisoa haholo indastering ea tšepe ea arc. Li-electrode tsa graphite li ka fana ka maemo a holimo a motlakase le bokhoni ba ho boloka maemo a phahameng haholo a mocheso o hlahisoang. Li-electrode tsa graphite li boetse li sebelisoa ho ntlafatseng tšepe le mekhoa e tšoanang ea ho qhibilihisa.
Packaging & Shipping
Lintlha tsa Pakete:Lepolanka Case/Pallets le likhoele tsa tšepe kapa Joalo ka litlhoko tsa bareki.
Boema-kepe:Tianjin Port, Qingdao Port.
Nako ea ho Etapele:E rometsoe ka matsatsi a 15-30 ka mor'a tefo.
Boemo ba Khoebo
Tianjin Eastmate Carbon Co., Ltd e sebakeng sa Tianjin City, e ikhethang ka ho romela mefuta e sa tšoaneng ea li-coke Chaena, ho akarelletsa le Graphite Electrode, petroleum coke, calcined coke, graphite petroleum coke joalo-joalo. Re khomarela "boleng ba pele" ho tiisa thepa ka theko ea tlhōlisano ka litlhaloso tse fapaneng, ka nako e le 'ngoe. Re ka boela ra etsa bonnete ba hore na u hloka bokae ka lebaka la limela tsa rona tse kholo tsa coke. Ehlile, re na le sehlopha sa rona sa thepa se ikhethileng ho fokotsa litšenyehelo ka ho fetesisa. Ka sehlopha se matla sa theknoloji, re ka lula re fana ka ts'ebeletso e tšepahalang ho etsa hore theko ea hau e be bonolo haholoanyane. Re ka fana ka litharollo indastering efe kapa efe moo matla e leng bohlokoa le ho ntlafatsa litšenyehelo.
![xq (4)rtz](https://ecdn6.globalso.com/upload/p/1003/image_other/2024-02/65c1a64e4758c49994.jpg)
LBH
1. Tlhaloso ea hau ha ea re tšoanela haholo.
Ka kopo, re fe matšoao a ikhethileng ka TM kapa lengolo-tsoibila. re tla u fa maikutlo kapele kamoo ho ka khonehang.
2.Nka fumana theko neng?
Re atisa ho qotsa ka hare ho lihora tse 24 ka mor'a ho fumana litlhoko tsa hau tse qaqileng, joalo ka boholo, bongata, joalo-joalo.
Haeba e le taelo e potlakileng, o ka re letsetsa ka kotloloho.
3. O fana ka mehlala?
E, lisampole lia fumaneha hore u hlahlobe boleng ba rona.
Nako ea ho fana ka mehlala e tla ba matsatsi a ka bang 3-10.
4. Ho thoe'ng ka nako ea pele ea lihlahisoa tse ngata?
Nako ea ho etella pele e ipapisitse le bongata, matsatsi a ka bang 7-15. Bakeng sa sehlahisoa sa graphite, sebelisa laesense ea lisebelisoa tse peli tse hlokang matsatsi a ka bang 15-20 a ho sebetsa.