0102030405
Graphite Electrodes e etsa morekisi ho tsoa Chaena
Tlhaloso ea Sehlahisoa
Ntho | Boleng |
Sebaka sa Oriqin | China |
Mofuta | Thibelo ea elektrode |
Kopo | Indasteri ea Metallurgical |
Bolelele | 2000mm-2700mm |
Khanyetso (u2.m | 4.0-8.8 |
Boima bo hlakileng(g/cm | 1.55-1,82 |
Themal Expansio | 1.1-2.6,1.1-1.4 |
Matla a Flexural (N/m2 | 28Mpa |
Lebitso la Sehlahiswa | UHP Kereiti ea Graphite Electrode |
Lintho tse tala | Petroleum Coke |
Colo | Ntsho |
Nnyo | 3TPI/4TPI/4TPIL |
Kopo | Smelting Stee |
MOQ | 20 Tor |
Deeistance/ | 4.8 ho isa ho 5.8 microns |
Boima bo hlakileng | 1.68-1,75 |
Matla a Flexural | 10-14 mpa |
Pacing | Linyeoe tsa Lehong |
RP | HP | UHP |
Electrode: | Electrode: | Electrode: |
Boima ba Bongata≥ 1.56g/cm3 | Boima ba Bongata≥ 1.65g/cm3 | Boima ba Bongata≥ 1.68g/cm3 |
Ho hanyetsa ka ho Khethehileng≤ 8.5μm | Ho hanyetsa ka ho Khethehileng≤ 6.5μm | Boiketlo bo khethehileng≤ 5.8μm |
Matla a ho Kobela≥ 10.0MPa | Matla a ho Kobela≥ 12.0MPa | Matla a ho Kobela≥ 16.0MPa |
Elastic Modulus≤ 9.3GPa | Elastic Modulus≤ 10.0GPa | Elastic Modulus≤ 14.0GPa |
Katoloso ea Mocheso≤ 2.7x10 -6/°C | Katoloso ea Mocheso≤ 2.2x10 -6/°C | Katoloso ea Mocheso≤ 1.9x10 -6/°C |
Molora≤0.5% | Molora≤0.3% | Molora≤0.2% |
Nipple: | Nipple: | Nipple: |
Boima ba Bongata≥ 1.68g/cm3 | Boima ba Bongata≥ 1.74g/cm3 | Boima ba Bongata≥ 1.76g/cm3 |
Tšimoloho e Khethehileng≤ 7.0μm | Ho hanyetsa ka ho Khethehileng≤ 5.5μm | Ho hanyetsa ka ho Khethehileng≤ 4.5μm |
Matla a ho Kobela≥ 14.0MPa | Matla a ho Kobela≥ 16.0MPa | Matla a ho Kobela≥ 18.0MPa |
Elastic Modulus≤ 13.7GPa | Elastic Modulus≤ 14.0GPa | Elastic Modulus≤ 16.0GPa |
Katoloso ea Mocheso≤ 2.5 x10 -6/°C | Katoloso ea Mocheso≤ 2.0 x10 -6/°C | Katoloso ea Mocheso≤ 1.4 x10 -6/°C |
Molora≤0.5% | Molora≤0.3% | Molora≤0.2% |
Graphite electrode e bua ka mofuta o phahameng oa mocheso o phahameng oa mocheso oa graphite o entsoeng ka coke ea petroleum le asphalt coke e le sekontiri le asphalt ea mashala e le sekontiri ka calcination e tala, ho sila le ho sila, ho kopanya, ho kopanya, ho bōpa, ho halika, ho kenya letsoho, graphitization le ho sebetsa ka mechine. , e bitsoang electrode ea maiketsetso ea graphite (e bitsoang electrode ea graphite).
Li-electrode tsa graphite li arotsoe ka Mefuta e 3: li-electrode tsa Graphite tsa RP, li-electrode tsa Graphite tsa HP, li-electrode tsa Graphite tsa UHP.
UHP Graphite Electrode. E entsoe ka coke ea nale ea boemo bo holimo 'me e phekoloa ka Lengthwise Graphitization (LWG). Thempereichara ea graphitization e ka fihla ho 2800 °C - 3000 °C. Lihlahisoa tse feliloeng li na le khanyetso e tlase ea motlakase & katoloso ea mela, e ntle ea ho hanyetsa mocheso oa mocheso le ho lumella letsoalo le leholo la hajoale.
HP Graphite Electrode. E amohela boleng ba petroleum coke kapa coke ea nale ea boemo bo tlase e le lisebelisoa tse tala. Thepa ea eona ea 'mele le ea mochini e phahame ho feta RP graphite electrode joalo ka khanyetso e tlase ea motlakase le ho lumella letsoalo le leholo la hajoale.
RP Graphite Electrode. E tloaelehileng grade petroleum coke e amoheloa bakeng sa tlhahiso. Mofuta ona oa electrode ea graphite o tšoaroa ka mocheso o tlase oa graphitization. Boima ba hona joale bo lumelletsoeng bo tlase ho feta li-electrode tsa HP graphite. Li-electrode tse tloaelehileng tsa graphite li hlalositsoe ka bongata bo lumelletsoeng ka tlase ho t han 17 A/cm2.
Kopo
Li-electrode tsa graphite li sebelisoa haholo ka seboping sa motlakase sa arc. Hona joale ke tsona feela lihlahisoa tse fumanehang tse nang le maemo a phahameng a motlakase le bokhoni ba ho boloka mocheso o phahameng haholo o hlahisoang ho EAF. Li-electrode tsa graphite li boetse li sebelisetsoa ho hloekisa tšepe ka har'a libopi tsa ladle le lits'ebetsong tse ling tsa ho qhibilihisa.
Packaging & Shipping
Lintlha tsa Pakete:Lepolanka Case/Pallets le likhoele tsa tšepe kapa Joalo ka litlhoko tsa bareki.
Boema-kepe:Tianjin Port, Qingdao Port.
Nako ea ho Etapele:E rometsoe ka matsatsi a 15-30 ka mor'a tefo.
BOCHABELA Molemo
Tianjin Eastmate Carbon Co., Ltd e sebakeng sa Tianjin City, e ikhethang ka ho romela mefuta e fapaneng ea li-cokes naheng ea China, ho kenyeletsoa Graphite Electrode, petroleum coke, calcined coke, graphite petroleum coke, graphite electrode, artificial graphite anode material joalo-joalo. Re khomarela "boleng ba pele" ho tiisa thepa ka theko ea tlhōlisano ka litlhaloso tse fapaneng, ka nako e le 'ngoe. Re ka boela ra etsa bonnete ba hore na u hloka bokae ka lebaka la limela tsa rona tse kholo tsa coke. Ehlile, re na le sehlopha sa rona sa thepa se ikhethileng ho fokotsa litšenyehelo ka ho fetesisa. Ka sehlopha se matla sa theknoloji, re ka lula re fana ka ts'ebeletso e tšepahalang ho etsa hore theko ea hau e be bonolo haholoanyane. Re ka fana ka litharollo indastering efe kapa efe moo matla e leng bohlokoa le ho ntlafatsa litšenyehelo.
![xq (4)6q3](https://ecdn6.globalso.com/upload/p/1003/image_other/2024-02/65c1a64e4758c49994.jpg)
Khamphani ea rona e na le metheo e mehlano e meholo ea tlhahiso, ho kenyelletsa Lanzhou e Gansu, Linyi e Shandong, Binhai e Tianjin, Ulanqab e Inner Mongolia, le Binzhou e Shandong. Tlhahiso ea selemo ke lithane tse 200,000 tsa coke e calcined, lithane tse 150,000 tsa graphitized carburizer, le lithane tse 20,000 tsa silicon carbide, 80,000 ea thepa ea maiketsetso ea graphite anode, 80,000 ea carbon & graphite electrode, le lihlahisoa tse ling tsa carbonite paste, electrograph, joalo-joalo.
![fff1cps](https://ecdn6.globalso.com/upload/p/1003/image_other/2024-02/65e02a64a956d36379.jpg)
![ff2f7j](https://ecdn6.globalso.com/upload/p/1003/image_other/2024-02/65e02a6c7ef4d58442.jpg)
LBH
1. Tlhaloso ea hau ha ea re tšoanela haholo.
Ka kopo, re fe matšoao a ikhethileng ka TM kapa lengolo-tsoibila. re tla u fa maikutlo kapele kamoo ho ka khonehang.
2. Nka fumana theko neng?
Re atisa ho qotsa ka hare ho lihora tse 24 ka mor'a ho fumana litlhoko tsa hau tse qaqileng, joalo ka boholo, bongata, joalo-joalo.
Haeba e le taelo e potlakileng, o ka re letsetsa ka kotloloho.
3. O fana ka mehlala?
E, lisampole lia fumaneha hore u hlahlobe boleng ba rona.
Nako ea ho fana ka mehlala e tla ba matsatsi a ka bang 3-10.
4. Ho thoe'ng ka nako ea pele ea lihlahisoa tse ngata?
Nako ea ho etella pele e ipapisitse le bongata, matsatsi a ka bang 7-15. Bakeng sa sehlahisoa sa graphite, sebelisa laesense ea lisebelisoa tse peli tse hlokang matsatsi a ka bang 15-20 a ho sebetsa.