Graphite Electrodes na-arụpụta ndị na-ebu si China
Nkọwa ngwaahịa
Ihe | Uru |
Ebe Oriqin | China |
Ụdị | Ihe mgbochi electrode |
Ngwa | Ụlọ ọrụ metallurgical |
Ogologo | 2000mm-2700mm |
Nguzogide (u2.m | 4.0-8.8 |
Njupụta pụtara ìhè (g/cm | 1.55-1.82 |
Themal Expansio | 1.1-2.6,1.1-1.4 |
Ike Flexural (N/m2 | 28Mpa |
Aha ngwaahịa | UHP Grade Graphite Electrode |
Akụrụngwa | Petroleum Coke |
Kọlọ | Nwa |
Ọnụ ara | 3TPI/4TPI/4TPIL |
Ngwa | Stee na-agbaze |
MOQ | 20 Tor |
Obi ike | 4.8 ruo 5.8 microns |
Njupụta pụtara ìhè | 1.68-1.75 |
Ike Flexural | 10-14mpa |
Pacing | Akpa osisi |
RP | HP | UHP |
Electrode: | Electrode: | Electrode: |
Nnukwu njupụta≥ 1.56g/cm3 | Nnukwu njupụta≥ 1.65g/cm3 | Nnukwu njupụta≥ 1.68g/cm3 |
Specific Resistivity≤ 8.5μm | Specific Resistivity≤ 6.5μm | Ngwọta a kapịrị ọnụ≤ 5.8μm |
Ehulata Ike≥ 10.0MPa | Ehulata Ike≥ 12.0MPa | Ehulata Ike≥ 16.0MPa |
Modulus Elastic ≤ 9.3GPa | Modulus Elastic≤ 10.0GPa | Modulus Elastic≤ 14.0GPa |
Ọnụego Mgbasawanye okpomọkụ≤ 2.7x10 -6/°C | Ọnụ ego Mgbasawanye okpomọkụ≤ 2.2x10 -6/°C | Ọnụego Mgbasawanye okpomọkụ≤ 1.9x10 -6/°C |
Ash≤0.5% | Ash≤0.3% | Ash≤0.2% |
Ọnụ ara: | Ọnụ ara: | Ọnụ ara: |
Nnukwu njupụta≥ 1.68g/cm3 | Nnukwu njupụta≥ 1.74g/cm3 | Nnukwu njupụta≥ 1.76g/cm3 |
Specific Resistivity≤ 7.0μm | Specific Resistivity≤ 5.5μm | Specific Resistivity≤ 4.5μm |
Ehulata Ike≥ 14.0MPa | Ehulata Ike≥ 16.0MPa | Ehulata Ike≥ 18.0MPa |
Modulus na-agbanwe ≤ 13.7GPa | Modulus Elastic≤ 14.0GPa | Modulus na-agbanwe ≤ 16.0GPa |
Ọnụego Mgbasawanye okpomọkụ≤ 2.5 x10 -6/°C | Ọnụego Mgbasawanye okpomọkụ≤ 2.0 x10 -6/°C | Ọnụego Mgbasawanye okpomọkụ≤ 1.4 x10 -6/°C |
Ash≤0.5% | Ash≤0.3% | Ash≤0.2% |
Graphite electrode na-ezo aka a ụdị elu-okpomọkụ graphite conductive ihe mere nke petroleum coke na asphalt coke dị ka mkpokọta na coal asphalt dị ka ihe nkedo site raw material calcination, egwepịa na egweri, batching, ịgwakọta, ịkpụzi, amịkpọ, impregnation, graphitization na n'ibu nhazi. , nke a na-akpọ electrode graphite artificial (nke a na-akpọ graphite electrode).
E kewara graphite electrodes n'ime ụdị atọ: RP Graphite electrodes, HP Graphite electrodes, UHP Graphite electrodes.
UHP Graphite Electrode. A na-eji coke agịga dị elu mee ya ma jiri Lengthwise Graphitization (LWG) gwọọ ya. Okpomọkụ eserese nwere ike iru 2800 Celsius - 3000 Celsius. Ngwaahịa emechara nwere nguzogide eletrik dị ala & mgbasawanye linear, ezigbo nguzogide ujo na-ekwe ka njupụta dị ugbu a buru ibu.
HP Graphite Electrode. Ọ na-ewere coke mmanụ ala dị mma ma ọ bụ coke agịga dị ala dị ka akụrụngwa. Njirimara anụ ahụ na akụrụngwa ya dị elu karịa RP graphite electrode dị ka obere nguzogide eletriki na ikwe ka njupụta dị ugbu a dị ukwuu.
RP Graphite Electrode. A na-anabata coke mmanụ ala nkịtị maka mmepụta. A na-emeso ụdị electrode graphite na obere okpomọkụ graphitization. Njupụta ugbu a ekwe ekwe dị ala karịa nke HP graphite electrode. A na-akọwapụta electrodes ike graphite mgbe niile na njupụta ugbu a na-ekwe ka obere t han 17 A/cm2.
Ngwa
A na-ejikarị eletrọd graphite eme ihe n'ọkụ ọkụ eletrik. Ha bụ naanị ngwaahịa dị ugbu a nwere oke ọkụ eletrik na ikike nke ịkwado oke okpomọkụ dị na EAF. A na-ejikwa electrodes graphite mee ka ígwè dị ọcha n'ime ọkụ ladle na usoro mgbaze ndị ọzọ. Ọ na-arụ ọrụ dị mkpa na mpaghara mmepụta okpomọkụ dị elu dị ka ígwè na ígwè smelting, electrolytic aluminum, ferroalloy, calcium carbide, silicon Industrial na yellow phosphorus smelting.
Nkwakọ ngwaahịa & Mbupu
Nkọwa ngwugwu:Osisi osisi / pallets nwere mpempe ígwè ma ọ bụ dị ka ihe ndị ahịa chọrọ.
Port:Tianjin Port, Qingdao Port.
Oge ndu:Ebupu na 15-30 ụbọchị mgbe ugwo.
Uru EASTMATE
Tianjin Eastmate Carbon Co., Ltd dị na Tianjin City, nke bụ ọkachamara na mbupụ iche nke cokes na China, gụnyere Graphite Electrode, mmanụ ala coke, calcined coke, graphite petroleum coke, graphite electrode, artificial graphite anode ihe na na. Anyị na-arapara na "mma mbụ" iji kwe nkwa ngwaahịa na ọnụahịa asọmpi na nkọwa dị iche iche, n'otu oge ahụ. Anyị nwekwara ike hụ na ọnụ ọgụgụ ị chọrọ n'ihi nnukwu osisi coke anyị. N'ezie, anyị nwere nke anyị pụrụ iche logistics otu iji belata ọnụ ahịa na kacha. Site na ndị otu teknụzụ siri ike, anyị nwere ike ịnye ọrụ a pụrụ ịdabere na ya mgbe niile iji mee ka ịzụrụ gị dị mfe karị. Anyị nwere ike ịnye ngwọta maka ụlọ ọrụ ọ bụla ebe ike dị mkpa na njikarịcha ọnụ ahịa ga-ekwe omume.
![xq (4)6q3](https://ecdn6.globalso.com/upload/p/1003/image_other/2024-02/65c1a64e4758c49994.jpg)
Ụlọ ọrụ anyị nwere isi mmepụta ihe ise, gụnyere Lanzhou na Gansu, Linyi na Shandong, Binhai na Tianjin, Ulanqab na Inner Mongolia, na Binzhou na Shandong. Ihe mmepụta kwa afọ bụ tọn 200,000 calcined coke, 150,000 tọn graphitized carburizer, na 20,000 tọn silicon carbide, 80,000 nke artificial graphite anode material, 80,000 carbon & graphite electrode, na ndị ọzọ carbon ngwaahịa gụnyere carbon electrode crucite crucite.
![ff1cps](https://ecdn6.globalso.com/upload/p/1003/image_other/2024-02/65e02a64a956d36379.jpg)
![ff2f7j](https://ecdn6.globalso.com/upload/p/1003/image_other/2024-02/65e02a6c7ef4d58442.jpg)
FAQ
1. Nkọwapụta gị adịghị mma maka anyị.
Biko nye anyị ihe ngosi akọwapụtara site na TM ma ọ bụ email. anyị ga-enye gị nzaghachi ozugbo enwere ike.
2. Kedu mgbe m nwere ike nweta ọnụahịa ahụ?
Anyị na-ehotakarị n'ime awa 24 mgbe ị nwetachara ihe achọrọ zuru ezu, dị ka nha, ọnụọgụ wdg.
Ọ bụrụ na ọ bụ iwu ngwa ngwa, ị nwere ike ịkpọ anyị ozugbo.
3. Ị na-enye samples?
Ee, ihe nlele dị maka ịlele ogo anyị.
Oge nnyefe sample ga-abụ ihe dịka ụbọchị 3-10.
4. Kedu maka oge ndu maka ngwaahịa oke?
Ogologo oge ọgwụgwọ dabere na ọnụọgụ, ihe dịka ụbọchị 7-15. Maka ngwaahịa graphite, tinye akwụkwọ ikike ihe eji eme ihe abụọ chọrọ ihe dịka ụbọchị ọrụ 15-20.